Hk. Lee et al., THE CHARACTERISTICS OF SYNTHESIZED POTASSIUM HEXATITANATE AND THE MANUFACTURING PROCESS OF THE MATRIX, Materials chemistry and physics, 45(3), 1996, pp. 243-247
The characteristics of synthesized potassium hexatitanate (K2O . 6TiO(
2)) and the manufacturing process of the matrix for an alkaline fuel c
ell were studied. Potassium hexatitanate was synthesized by sintering
a mixture of K2CO3 and TiO2 at 850 degrees C, and the thin film type m
atrix was manufactured with polytetrafluoroethylene (PTFE) as the bind
er. The highest wettability, 50%, was obtained for the matrix manufact
ured using 12 h ball-milled powder containing 10 wt.% PTFE, and it als
o showed good mechanical properties. The matrix made using K2O . 6TiO(
2) whiskers showed 165% wettability. The wettability, bubble pressure
and porosity of the matrix made using a 1:2 powder:whisker mixture wer
e 140%, 220 mmHg and 62%, respectively.