S. Maschio et G. Farne, THERMAL-SHOCK RESISTANCE OF MATERIALS BASED ON CEO2-STABILIZED TETRAGONAL ZIRCONIA POLYCRYSTALS, Materials chemistry and physics, 37(2), 1994, pp. 136-140
Materials based on tetragonal zirconia polycrystals fully stabilized w
ith CeO2 have been prepared starting from commercial powders. The mech
anical properties of samples with different compositions were measured
at room temperature and after quench tests. The effects of thermal tr
eatments on the microstructure and crystal phases and their detrimenta
l influence on strength, toughness and hardness were evaluated. Experi
ments demonstrated that residual porosity and higher amounts of ceria
favourably influence the retention of material properties after therma
l treatment.