Dp. Shumov et al., HIGH-TEMPERATURE SOLUTIONS SUITABLE FOR THE GROWTH OF NDAL3(BO3)(4) CRYSTALS, Journal of crystal growth, 172(3-4), 1997, pp. 478-485
The concentration region of the NdAl3(BO3)(4) phase in the NdBO3-AlBO3
-BaO . 2B(2)O(3) system was determined. The experimental data obtained
make possible the choice of the most suitable region of high-temperat
ure solutions for the growth of NdAl3(BO3)(4) single crystals. This re
gion is between mole ratios of NdBO3:AlBO3=1:2 and 1:3. The best quali
ty crystals were grown from solution with a mole ratio of NdBO3:AlBO3=
1:2 by spontaneous crystallization. The electronmicroscopy, X-ray powd
er diffraction and DTA characterization of the NdAl3(BO3)(4) single cr
ystals have been performed.