H. Shimbo et al., GROWTH AND CHARACTERIZATION OF NOVEL MGSE ZNCDSE SUPERLATTICE QUASI-QUATERNARIES ON INP SUBSTRATES/, Journal of crystal growth, 185, 1998, pp. 16-20
Novel MgSe/ZnCdSe superlattice quasi-quaternaries (SL-QQs) lattice-mat
ched to (1 0 0) InP substrates were grown by molecular beam epitaxy fo
r the first time. From the X-ray diffraction measurements of the SL-QQ
s, it was made sure that the designed superlattice periods were actual
ly obtained. While, the equivalent Mg composition of the SL-QQs was co
ntrolled from 0.12 to 0.60 by changing the MgSe layer thickness ratio
to the superlattice period. Optical properties of the SL-QQs were inve
stigated by photoluminescence (PL) and reflectance measurements at 15
K. As a result, the PL peak energies of the SL-QQs monotonically incre
ased from 2.24 to 2.91 eV with increasing the Mg composition from 0.12
to 0.60 like MgZnCdSe bulk compounds. (C) 1998 Elsevier Science B.V.
All rights reserved.