The physicochemical properties of La0.6Sr0.4Mn1-xFexO3 solid solutions
are studied. It is found that the polarization resistance of La0.6Sr0
.4Mn1-xFexO3 electrode layers can be substantially reduced by sequenti
ally coating the electrode surface with praseodymia and lanthanum stro
ntium cobaltate layers.